Cracks found in 3 more Southwest jets

YUMA, Ariz. -- Three more Southwest Airlines jetliners have small, subsurface cracks that are similar to the cracks suspected of playing a role in the fuselage tear of a Boeing 737-300, causing the aircraft to lose pressure and forcing a frightening emergency landing, officials say.

The latest fissures were found after airline's 737-300 fleet was grounded. Checks on the remaining jets are expected to be completed by late Tuesday, the airline said. That means flight cancellations will likely continue until the planes are back in the air. About 600 flights in all were canceled over the weekend after Southwest grounded 79 of its planes.

The five-foot-long hole tore open in the passenger cabin roof area Friday afternoon shortly after the plane left Phoenix for Sacramento, Calif. None of the 118 people aboard was seriously hurt as the plane descended from 34,400 feet to a military base in Yuma, 150 miles southwest of Phoenix.

Since then Southwest has grounded its 79 other Boeing 737-300s and begun inspecting them.

Sunday night, another Southwest Boeing jet was diverted, this time because of a burning electrical smell in the passenger cabin, Southwest and Los Angeles Airport officials said. The airline said the problem was not related to the fuselage cracks.

The plane carrying 142 people was en route Sunday evening from Oakland, Calif., to San Diego, when it made an unscheduled landing in Los Angeles, where passengers changed planes and continued on their journeys, Southwest spokeswoman Whitney Eichinger said. No one was hurt.

She said the cause of electrical smell is being investigated, but it "was completely unrelated to the issue in Arizona." She said Sunday's aircraft was also a Boeing 737 but she didn't know if it was the 737-300.

In its statement on the inspections, Southwest said Sunday that two planes have been found to have cracks similar to those in the stricken aircraft and will be evaluated and repaired before they are returned to service.

A National Transportation Safety Board member told The Associated Press later that a third plane had been found with cracks developing.

The cracks found in the three planes developed in two lines of riveted joints that run the length of the aircraft. The agency is focusing its probe on the area of the cracks but has not determined that the cracks caused the rupture.

NTSB board member Robert Sumwalt said Boeing was developing a "service bulletin" for all 737-300 models with comparable flight cycle time as the Arizona jet, which was 15 years old and had about 39,000 takeoff and landing cycles.

There are 931 such models in service worldwide, 288 of which are in the U.S. fleet.

Boeing's bulletin would strongly suggest extensive checks of two lines of "lap joints" that run the length of the fuselage. The NTSB has not mandated the checks, but Sumwalt said the FAA is likely to make them mandatory.

The tear along a riveted "lap joint" near the roof of the stricken plane above the midsection shows evidence of extensive cracking that hadn't been discovered during routine maintenance before the flight -- and probably wouldn't have been unless mechanics specifically looked for it -- officials said.

"What we saw with Flight 812 was a new and unknown issue," Mike Van de Ven, Southwest executive vice president and chief operating officer, said. "Prior to the event regarding Flight 812, we were in compliance with the FAA-mandated and Boeing-recommended structural inspection requirements for that aircraft."

Sumwalt said that the rip was a foot wide, and that it started along a joint where two sections of the plane's skin are riveted together. An examination showed extensive pre-existing damage along the entire tear. Further inspection found more cracks in areas that had not torn open.

The riveted joints that run the length of the plane were previously not believed to be a fatigue problem and not normally subjected to extensive checks, Sumwalt said.

"Up to this point only visual inspections were required for 737s of this type because testing and analysis did not indicate that more extensive testing was necessary," Sumwalt said.

That will likely change after Friday's incident, he said.

The FAA declined to say if it was requiring other operators to check their aircraft for similar flaws.

Federal records show cracks were found and repaired a year ago in the frame of the same Southwest plane.

A March 2010 inspection found 10 instances of cracking in the aircraft frame, which is part of the fuselage, and another 11 instances of cracked stringer clips, which help hold the plane's skin on, according to an AP review of FAA records of maintenance problems for the Arizona plane.

The records show the cracks were either repaired or the damaged parts replaced. Cracking accounted for a majority of the 28 problem reports filed as a result of that inspection.

It's common for fuselage cracks to be found during inspections of aging planes, especially during scheduled heavy-maintenance checks in which planes are taken apart so that inspectors can see into areas not normally visible.

The Arizona jetliner had gone through about 39,000 cycles of pressurizing, generally a count of takeoffs and landings. Cracks can develop from the constant cycle of pressurizing for flight, then releasing the pressure.

Southwest officials said it had undergone all inspections required by the FAA. They said the plane was given a routine inspection Tuesday and underwent its last so-called heavy check, a more costly and extensive overhaul, in March 2010.

The decompression happened about 18½ minutes after takeoff from Phoenix Sky Harbor Airport after the pilots reached their cruising altitude. They immediately donned their oxygen masks, declared an emergency and briefly considered returning to Phoenix before the cabin crew told them of the extent of the damage, Sumwalt said.

"They discussed landing in Phoenix, but quickly upon getting the assessment decided to divert to Yuma because it was the closest suitable airport," he said.

The plane's voice and data recorders were being examined in Washington.